CTH: YAG Makristasi
Ho,Cr,Tm:YAG -yttrium aluminium garnet laser makristasi akaiswa chromium,thulium uye holmium ions kuti ape lasing pa2.13 microns ari kuwana mamwe maapplication,kunyanya muindasitiri yezvokurapa. anoshandisa YAG semuenzi.YAG's yemuviri, inopisa uye yemaziso zvimiro zvinonyatsozivikanwa uye zvinonzwisiswa nechero laser mugadziri.Iyo ine yakafara maapplication mukuvhiya, mazino, kuyedza kwemuchadenga, nezvimwe.
Zvakanakira zveCTH:YAG:
• High kutsetseka kushanda zvakanaka
• Kupombwa nemwenje wemwenje kana diode
• Inoshanda zvakanaka pane tembiricha yemumba
• Inoshanda munzvimbo isina njodzi yewavelength
Dopant Ion
| Cr3+ Concentration | 0.85% |
| Tm3+ Concentration | 5.9% |
| Ho3+ Concentration | 0.36% |
Operating Spec
| Emission Wavelength | 2.080 um |
| Laser Transition | 5I7→5I8 |
| Flouresence Hupenyu hwose | 8.5 ms |
| Pombi Wavelength | flash rambi kana diode pumped @ 780nm |
Basic Properties
| Coefficient of Thermal Expansion | 6.14 x 10-6K-1 |
| Thermal Diffusivity | 0.041 cm2s-2 |
| Thermal Conductivity | 11.2 W m-1K-1 |
| Chaicho Kupisa (Cp) | 0.59 J g-1K-1 |
| Thermal Shock Resistant | 800 W m-1 |
| Refractive Index @ 632.8 nm | 1.83 |
| dn/dT (Thermal Coefficient of Refractive Index) @ 1064nm | 7.8 10-6K-1 |
| Melting Point | 1965 ℃ |
| Density | 4.56 g cm-3 |
| MOHS Kuoma | 8.25 |
| Crystal Structure | Cubic |
| Standard Orientation | <111> |
| Y3+ Saiti Symmetry | D2 |
| Lattice Constant | a=12.013 Å |
| Molecular Weight | 593.7 g mol-1 |
Technical Parameters
| Wavefront Distortion | ≤0.125ʎ/inch@1064nm |
| Tsvimbo Size | Diameter: 3-6mm, Kureba: 50-120mm, Pakukumbira kwemutengi |
| Dimensional Tolerances | Diameter: ± 0.05mm Kureba: ± 0.5mm |
| Bharel Finish | Kupera kwepasi:400 #Grit |
| Parallelism | <30″ |
| Perpendicularity | ≤5′ |
| Flatness | ʎ/10 |
| Surface Quality | 10/5 |
| AR coating Reflectivity | ≤0.25%@2094nm |
-