• ZGP(ZnGeP2) Makristasi

    ZGP(ZnGeP2) Makristasi

    ZGP makristasi ane mahombe asina mutsara coefficients (d36 = 75pm/V), yakafara infrared transparency range (0.75-12μm), high thermal conductivity (0.35W/(cm·K)), yakakwira laser kukuvara chikumbaridzo (2-5J/cm2) uye zvakanaka machining zvivakwa, ZnGeP2 crystal yainzi mambo we infrared nonlinear optical crystals uye ichiri yakanakisa frequency kushandura zvinhu kune yakakwirira simba, tunable infrared laser chizvarwa.Tinogona kupa mhando yepamusoro yemaziso uye dhayamita hombe ZGP makristasi ane akanyanya kuderera absorption coefficient α <0.05 cm-1 (papombi wavelengths 2.0-2.1 µm), inogona kushandiswa kugadzira yepakati-infrared tunable laser ine hunyanzvi hwepamusoro kuburikidza neOPO kana OPA. maitiro.

  • AGSe(AgGaSe2) Makristasi

    AGSe(AgGaSe2) Makristasi

    AGSeAgGaSe2 makristasi ane bhendi mupendero pa 0.73 uye 18 µm.Hunhu hwayo hwekufambisa hunobatsira (0.9–16 µm) uye hupamhi hwekuenzanisa nhanho inopa yakanakisa mikana yeOPO maapplication kana yapombwa neakasiyana siyana lasers.Tuning mukati me2.5–12 µm yawanikwa pakupomba neHo:YLF laser pa2.05 µm;pamwe chete neasiri-yakakosha phase matching (NCPM) kushanda mukati me1.9–5.5 µm pakupomba pa1.4–1.55 µm.AgGaSe2 (AgGaSe2) yakaratidzwa kuve inoshanda frequency yakapetwa kaviri kristaro kune infrared CO2 lasers mwaranzi.

  • AGS(AgGaS2) makristasi

    AGS(AgGaS2) makristasi

    AGS iri pachena kubva pa0.50 kusvika 13.2 µm.Kunyange zvazvo nonlinear optical coefficient iri yakaderera pakati peakataurwa infrared crystals, high short wavelength transparency edging pa550 nm inoshandiswa mumaOPO anopombwa neNd:YAG laser;mune akawanda mutsauko frequency kusanganisa kuedza ne diode, Ti: Sapphire, Nd: YAG uye IR dhayi lasers inovhara 3-12 µm renji;mune yakananga infrared countermeasure masisitimu, uye yeSHG yeCO2 laser.Thin AgGaS2 (AGS) mahwendefa ekristaro akakurumbira kune ultrashort pulse chizvarwa pakati IR renji nemusiyano frequency chizvarwa chinoshandisa NIR wavelength pulses.

  • BGSe(BaGa4Se7) Makristasi

    BGSe(BaGa4Se7) Makristasi

    Makristasi epamusoro-soro eBGSe (BaGa4Se7) ndiyo selenide analogue yechalcogenide compound BaGa4S7, iyo acentric orthorhombic structure yakaonekwa muna 1983 uye iyo IR NLO effect yakashumwa muna 2009, ichangobva kugadzirwa IR NLO crystal.Yakawanikwa kuburikidza neiyo Bridgman-Stockbarger maitiro.Iyi kristaro inoratidza kutapurirana kwepamusoro pamusoro pehupamhi hwe0.47-18 μm, kunze kweiyo peak yekunyudza inosvika 15 μm.

  • BGGSe(BaGa2GeSe6) Makristasi

    BGGSe(BaGa2GeSe6) Makristasi

    Iyo BaGa2GeSe6 crystal ine yakakwira optical kukuvara pachikumbaridzo (110 MW/cm2), yakafara spectral transparency range (kubva pa0.5 kusvika 18 μm) uye yakakwira isina mutsara (d11 = 66 ± 15 pm/V) , izvo zvinoita kuti kristaro iyi inakidze zvakanyanya frequency kushandurwa kwelaser radiation kuita (kana mukati) yepakati-IR renji.

  • GaSe Crystal

    GaSe Crystal

    Gallium Selenide (GaSe) isina-linear optical single crystal, ichibatanidza yakakura isina-mutsara coefficient, yakakwirira kukuvara kwechikumbaridzo uye yakafara kujeka.Icho chinhu chakanyatsokodzera zvinhu zveSHG mukati me-IR.